DEVELOPMENT AND PRODUCTION OF CERAMIC TILES FROM WASTE BOTTLE POWDER (MILLED GLASS)

Authors

  • Z. U. Elakhame Federal Institute of Industrial Research, Oshodi, Lagos
  • F. Ifebhor Federal Institute of Industrial Research, Oshodi, Lagos
  • W. A. Asotah Federal Institute of Industrial Research, Oshodi, Lagos

DOI:

https://doi.org/10.3126/kuset.v12i2.21521

Keywords:

Clay, Milled glass, Ceramics, Tiles

Abstract

 Ceramic tiles were produced from a varying mixture of clay and milled glass and the physio-chemical properties of the samples were determined. 0–70% weight milled glass was added to clay mineral. Seven samples were obtained before the clay which serves as binder was not able to hold the mixture together. It was discovered that the porosity of the tiles increased as the percentage weight of the clay material decreased and milled glass increased. Also, the compressive strength of the tiles peaked at sample 5 (60% clay & 40% milled glass). Results obtained showed that samples containing from 30-60% weight of milled glass in proportion with clay percentage had the best formulation properties.

 Kathmandu University

Journal of Science, Engineering and Technology

Vol. 12, No. 2, 2016, page: 50-59

 

Downloads

Download data is not yet available.
Abstract
552
PDF
1623

Downloads

Published

2016-12-01

How to Cite

Elakhame, Z. U., Ifebhor, F., & Asotah, W. A. (2016). DEVELOPMENT AND PRODUCTION OF CERAMIC TILES FROM WASTE BOTTLE POWDER (MILLED GLASS). Kathmandu University Journal of Science, Engineering and Technology, 12(2), 50–59. https://doi.org/10.3126/kuset.v12i2.21521

Issue

Vol. 12 No. 2 (2016)

Section

Original Research Articles

License

This license enables reusers to distribute, remix, adapt, and build upon the material in any medium or format, so long as attribution is given to the creator. The license allows for commercial use. If you remix, adapt, or build upon the material, you must license the modified material under identical terms.