Structural and Optical Characterization of Zinc Oxide Films Prepared By Two Stage; Spin Coating and Hydrothermal Process

Authors

  • Laxmi Dangol Physics Department, Amrit Science Campus, Tribhuvan University, Kathmandu
  • Leela Pradhan Joshi Physics Department, Amrit Science Campus, Tribhuvan University, Kathmandu

DOI:

https://doi.org/10.3126/jist.v21i1.16051

Keywords:

Thin film, Zinc oxide, Band gap, XRD, SEM

Abstract

Thin films of Zinc Oxide (ZnO) of average thickness 364 nm were deposited on glass substrates via hydrothermal process using a mixture of 25 mM aqueous solutions of zinc nitrate and hexamethylenetetramine at a constant temperature of 75 ± 5°C. The structure of ZnO film was analyzed by using X-ray diffraction (XRD). Our result showed that ZnO film is of polycrystalline nature with preferential orientation along (002) perpendicular to the substrate. Average crystallite size of prepared ZnO film was found to be 18 nm. The Scanning Electron Microscope (SEM) image clearly showed the growth of nano-plate structure with an average thickness and breadth of 90 nm and 390 nm respectively. The band gap of ZnO was determined from transmittance spectrum captured in the visible wavelength. The calculated value of direct band gap was 3.24 eV.

Journal of Institute of Science and Technology

Vol. 21, No. 1, 2016, page: 61-64

 

Downloads

Download data is not yet available.
Abstract
719
PDF
2171

Downloads

Published

2016-11-24

How to Cite

Dangol, L., & Joshi, L. P. (2016). Structural and Optical Characterization of Zinc Oxide Films Prepared By Two Stage; Spin Coating and Hydrothermal Process. Journal of Institute of Science and Technology, 21(1), 61–64. https://doi.org/10.3126/jist.v21i1.16051

Issue

Vol. 21 No. 1 (2016)

Section

Research Papers

License

The views and interpretations in this journal are those of the author(s). They are not attributable to the Institute of Science and Technology, T.U. and do not imply the expression of any opinion concerning the legal status of any country, territory, city, area of its authorities, or concerning the delimitation of its frontiers of boundaries.

The copyright of the articles is held by the Institute of Science and Technology, T.U.