Influence of Annealing on Creep Indentation, Surface Properties and Electrochemical Corrosion Behavior of Ni-Cr Based Dental Alloy

Authors

  • Abu Bakr El-Bediwi Physics Department, Faculty of Science, Mansoura University
  • Eman Kashita Qassim University, Ministry of High Education
  • Salah M.M. Salman Physics Department, Faculty of Science, Helwan University, Ain-Helwan

DOI:

https://doi.org/10.3126/ijasbt.v5i3.18295

Keywords:

microstructure, Vickers hardness, roughness parameters, corrosion, creep

Abstract

Heat treatment is a process in which alloy is heated to get different microstructures and desired properties associated with it which may affect the corrosion rate, nature form and size.  Effect of annealing on microstructure, creep indentation, hardness and electrochemical corrosion behavior of Ni63Cr24.6Mo10.8Si1.5Mn0.06C0.04 alloy were investigated.  Microstructure of Ni63Cr24.6Mo10.8Si1.5Mn0.06C0.04 alloy changed after annealing at different temperature for two hours.  Crystal size of nickel in matrix alloy increased after annealing for two hours at different temperature.  Stress exponent, n, Vickers hardness and calculated maximum shear stress of Ni63Cr24.6Mo10.8Si1.5Mn0.06C0.04 alloy decreased after annealing. Corrosion rate of Ni63Cr24.6Mo10.8Si1.5Mn0.06C0.04 alloy increased after annealing for two hours at different temperature. 

Int. J. Appl. Sci. Biotechnol. Vol 5(3): 366-374

Downloads

Download data is not yet available.
Abstract
719
PDF
662

Downloads

Published

2017-09-27

How to Cite

El-Bediwi, A. B., Kashita, E., & Salman, S. M. (2017). Influence of Annealing on Creep Indentation, Surface Properties and Electrochemical Corrosion Behavior of Ni-Cr Based Dental Alloy. International Journal of Applied Sciences and Biotechnology, 5(3), 366–374. https://doi.org/10.3126/ijasbt.v5i3.18295

Issue

Vol. 5 No. 3 (2017)

Section

Research Articles: Biological Sciences